GB/T700 Q235C hot rolled plates

GB/T700 Q235C hot rolled plates

FOB Reference Price:Get Latest Price

Offer Ability:5 000MT/Per Month GB/T700 Q235C hot rolled plates

  • Loading Port: Shanghai Tianjin Qingdao.
  • Delivery Time: 30-50 days 7 days for stock goods
  • Contact usOnline order

Product Description

GB/T700 Q235C hot rolled plates are produced in accordance with ASTM A283 in the United States. Q represents the yield of Q235C material, and the latter 235 refers to the yield value of Q235C material, which is about 235MP. The yield value will decrease with the increase of Q235C steel plates thickness. Due to its moderate carbon content and better comprehensive properties, the properties of Q235C hot rolled plates such as strength, plasticity and welding have been well matched and Q235C steel are widely used.

GB/T700 Q235C hot rolled plates chemical composition:

Grade C % Si % Mn % P % S %
Q235C ≤0.17 ≤0.35 ≤1.40 ≤0.040 ≤0.040

GB/T700 Q235C hot rolled plates mechanical property:

Grade Thickness Yield Strength (Mpa) Tensile Strength Elongation(%) Impact Energy
(mm) (MPa) Min
Q235C ≤ 16 235 370-500 26 0 27J
> 16-40 225 370-500 25 0 27J
>40 215 370-500 24 0 27J
The min impact energy is longitudinal energy

Q235C steel are often rolled into medium and thick GB/T700 Q235C hot rolled plates. Q235C hot rolled plates are widely used in architectural and engineering structures, to build building frame, high voltage transmission tower, bridge, vehicle, boiler, vessel, ships and so on. Q235C steel are also used as a mechanical part with less high performance requirements.

BBN Steel is specializing in GB/T700 Q235C hot rolled plates which is under GB/T specification.GB/T700 Q235C hot rolled plates has excellent mechanical properties and widely application. Combining above advantages can be supplied the most in line with customer requirements products. Moreover,we will provide cutting, pretreatment, galvanizing, testing, heat treatment services for GB/T700 Q235C hot rolled plates.If you want to known GB/T700 Q235C hot rolled plates more information,welcome to contact with us at any time:

BBN Service

1.Additional Condition: UT(Ultrasonic examination), AR(As Hot Rolled only), TMCP(Thermal Mechanical Control Processing), N(Normalized), Q+T(Quenched and Tempered),Z Direction Test(Z15,Z25,Z35), Charpy V-Notch Impact Test, The Third Party Test (such as SGS Test), Coated or Shot Blasting and Painting.

2.Shipping department: a).Book shipping space b).Documents confirmation c).Shipping track d).Shipping case

3.Production control department: a).Technical evaluation b).Production Schedule c).Production Tracking d).Successfully complaint case

4.Quality control: a).Test in mill b).Inspection before Shipment c).Third Party Inspection d).About Package problem e).Quality problem case

5.Customers’ feedback and complaint: a).Quality feedback b).Service feedback c).Complaint d).Case